Blast Furnance Slag is a by product of Steel Making Units using Blast furnance technology. This is the last remaining part of steel which is mostly used by Slag Cement manufacturers.
Labh Supplies various origin Blast Furnance Slag to cement industries locally manufacturing Slag cement.
| Material | Raw GBFS |
|---|---|
| Origin | Iran, China, India |
| MgO | Max 7.0% |
| Sum(CaO+MgO+SiO2) | Min 80% |
| Modulus(CaO+MgO)/(SiO2) | Min 1.20 |
| Modulus(CaO)/(SiO2) | Max 1.20 |
| Glass Content | Min 95% |
| Chloride | Max 0.1% |
| Moisture | Max 10.0% |
| Size (under 5 mm) | ≥99.0% |
| Material | Raw GBFS |
|---|---|
| Origin | Iran, China, India |
| MgO | Max 7.0% |
| Sum(CaO+MgO+SiO2) | Min 80% |
| Modulus(CaO+MgO)/(SiO2) | Min 1.20 |
| Modulus(CaO)/(SiO2) | Max 1.20 |
| Glass Content | Min 95% |
| Chloride | Max 0.1% |
| Sulphur (S2-) Sulphide | Max 1.50% |
| Moisture | Max 10.0% |
| Size (under 5 mm) | ≥99.0% |
| Physical Properties | |
|---|---|
| W/C Ratio | Max 0.45 |
| Air Content | Max 0.50% |
| Fineness Wet Sieve Retained at 45 Micron | Min 420 m2/Kg |
| Loss on Ignition | Max 2.00% |
| Activity Index at 07 days / at 28 days | 60% / 90% |
Capacity: 1 Million Ton/Year